Expanding Foam - 24oz
Why use FP200 FR Expanding Foam
- Extremely versatile solution
- CFC free
- Excellent fill capabilities
- Very easy to install and finish
- Excellent smoke and draft seal capabilities
- Sound dampening properties
- Paintable and stainable
- Easily trimmed after curing
- Excellent adhesion to most building substrates
- Unaffected by moisture or humidity when cured
- Cures to provide a strong semi-regid seal
Technical Information
Application Temperature:Min 41F (5C) Surface
68-77F (20C-25C) Can
Can must be inverted for dispensing
Flammable during dispensing
Tack free time:5-10 mins*
Cure time:20-25 mins 1.5" Dia (38mm)*
Hardening time:1.5 - 2 hrs*
Foam when cured has around 60% closed cell content
Specific gravity:22-26 kg/m3
Water absorption:max 1% volume
Temp. resistance:-40F to 194F (-40C to 90C)
Tensile strength:0,071 - 0,076 MPa
Elongation at break:15 - 20%
Free expansion:120%
* depending on temperature and humidity
Flame and smoke index:10 & 35, Class A rating
Flammability class:B1 according to DIN4102 part 1
Storage:9 months 5F to 68F (10C to 20C)
Higher temperatures can shorten storage life. Must be stored in vertical position (upright)
VOC:2% per Council Directive 1999/13/EC 23.6g/l
STC:38
Dielectric Constant (relative static permittivity) 1.2 R:7/inch (2.54 cm)
Application Temperature:Min 41F (5C) Surface
68-77F (20C-25C) Can
Can must be inverted for dispensing
Flammable during dispensing
Tack free time:5-10 mins*
Cure time:20-25 mins 1.5" Dia (38mm)*
Hardening time:1.5 - 2 hrs*
Foam when cured has around 60% closed cell content
Specific gravity:22-26 kg/m3
Water absorption:max 1% volume
Temp. resistance:-40F to 194F (-40C to 90C)
Tensile strength:0,071 - 0,076 MPa
Elongation at break:15 - 20%
Free expansion:120%
* depending on temperature and humidity
Flame and smoke index:10 & 35, Class A rating
Flammability class:B1 according to DIN4102 part 1
Storage:9 months 5F to 68F (10C to 20C)
Higher temperatures can shorten storage life. Must be stored in vertical position (upright)
VOC:2% per Council Directive 1999/13/EC 23.6g/l
STC:38
Dielectric Constant (relative static permittivity) 1.2 R:7/inch (2.54 cm)