T-HB1550Z - Polarizing Fiber for 1550 nm, Pricing Per Meter
T-HB1550Z - Polarizing Fiber for 1550 nm, Pricing Per Meter
Features
- ~100 nm Polarizing Window
- ≥30 dB Extinction Ratio
- Design Wavelength: 830, 1064, or 1550 nm
- Applications:
- Fiber Optic Gyroscopes
- Coherent Communications
- Current Sensors
- Operating Wavelength 1550 nm
- Cladding Diameter
- Coating Diameter 245 ± 15 µm
- Mode Field Diameter (MFD) is specified as a nominal value 10.0 - 12.5 µm @ 1550 nm
- Numerical Aperture (NA) is specified as a nominal value 0.9-0.11
- Cladding Index 1550 nm: 1.44683
- Core Index 1550 nm: 1.44402
- Cut-Off (Typ.) 1150 nm
- Attenuation ≤0.02 dB/m @ 1550 nm
- Beat Length ≤2.5 mm @ 1550 nm
- Extinction Ratio ≥30 dB
- 20 dB Fast Edge ≤1500 nm
- 3 dB Slow Edge ≥1600 nm
Fiber | HB1550Z |
---|---|
Operating Wavelength | 1550 nm |
Cladding Diamete | 125 ± 1 µm |
Coating Diameter | 245 ± 15 µm |
Mode Field Diameter | 10.0 - 12.5 µm @ 1550 nm |
Numerical Aperture | 0.9-0.11 |
Core Index | 1550 nm: 1.44683g |
Cladding Index | 1550 nm: 1.44402g |
Cut-Off Wavelength (Typical) | 1150 nm |
Attenuation | ≤0.02 dB/m @ 1550 nm |
Beat Length | ≤2.5 mm @ 1550 nm |
Extinction Ratio | ≥30 dB |
20 dB Fast Edge | ≤1500 nm |
3 dB Slow Edge | ≥1600 nm |
Core-Cladding Concentricity | ≤1 µm |
Coating-Cladding Offset | ≤10 µm |
Coating Material | Dual Acrylate |
Operating Temperature | -40 to 85 °C |
Proof Test Level | 1% (100 kpsi) |
Fiber | A | B | C | D |
---|---|---|---|---|
T-HB1550Z | 1550 nm Laser Source |
SMF-28-J9, CCC1310-J9, 1550BHP, or 1310BHP Fiber |
Coiled HB1550Z Fiber | Aligned PM1550-XP Fiber |