T-MF11L1AR1 - Ø100 µm, 0.26 NA, InF3 MM Patch Cable, ARC: 4.0 - 4.6 µm, SMA905, 1 m Long
T-MF11L1AR1 - Ø100 µm, 0.26 NA, InF3 MM Patch Cable, ARC: 4.0 - 4.6 µm, SMA905, 1 m Long
- Incorporates Fluoroindate (InF3) Fiber Manufactured at Thorlabs' Fiber Draw Facility
- Core Size: Ø100 µm
- Stiff, Ø3.0 mm Plastic Jacket and SMA905 Connectors
- Antireflection-Coated for for 4.0 - 4.6 µm
- <0.50% Average Reflection Loss
- Compatible with Visible-Wavelength Alignment Beams
- Fiber InF3 Multimode
- Operating Range 310 nm - 5.5 µm
-
Attenuation ≤0.25 dB/m (for 2.0 - 4.6 µm)
- Core Diameter 100 ± 2.0 µm
- Cladding Diameter 192 ± 2.5 µm
-
NA 0.26 ± 0.02 @ 2.0 µm
- Bend Radius (Short Term/ Long Term) ≥2.5 cm / ≥5 cm
- Connectors SMA905
- Jacket Blue PVDF (Ø3 mm)
- Operating Temp. -40 to 85 °C
Applications
- Spectroscopy
- Environmental Monitoring
- Chemical Sensing
- Systems Requiring Low Feedback
| MF11L1AR1 Specifications | |
|---|---|
| Connectors | SMA905 |
| Jacket | FT030DF-B |
| Fiber Type | Fluoroindate (InF3) |
| Transmission Range | 310 nm - 5.5 µm |
| Typical Attenuation | 0.1 dB/m @ 2.5 µm and 3.6 µm |
| Maximum Attenuation | ≤0.25 dB/m (from 2.0 to 4.6 µm) |
| NA | 0.26 ± 0.02 @ 2 µm |
| Typical Core Index | 1.487 @ 3.6 µm |
| Core Diameter | 100 ± 2.0 µm |
| Cladding Diameter | 192 ± 2.5 µm |
| Coating Diameter | 287 ± 15 µm |
| Core/Cladding Concentricity | ≤2 µm |
| Core Circularity | ≥98% |
| Long-Term Bend Radius | ≥5 cm |
| Short-Term Bend Radius | ≥2.5 cm |
| Operating Temperature | -40 to 85 °C |