T-NLC07 - Ø1" Mounted β-BBO Crystal, 3.00 mm Thick, θ = 19.8°, 1300 - 1700 nm Fund., 650 - 850 nm SHG
T-NLC07 - Ø1" Mounted β-BBO Crystal, 3.00 mm Thick, θ = 19.8°, 1300 - 1700 nm Fund., 650 - 850 nm SHG
- Mounted Crystal with Antireflection (AR) Coating for 650 - 850 nm and 1300 - 1700 nm
- Crystal Thickness 3.00 mm
- Crystal Thickness Tolerance ±0.05 mm
- Angle of Optic Axis (θ) 19.8°
- Tuning Angle vs. Wavelength
- Optic Axis Angle (θ)a Tolerance ±0.5°
- Fundamental Wavelength (1ω) AOI = 0° 1550 nm
- Fundamental Wavelength (1ω) AOI Tuned 1300 - 1700 nm
- SHG Wavelength (2ω) AOI = 0° 775 nm
- SHG Wavelength (2ω) AOI Tuned 650 - 850 nm
- Minimum Recommended Focal Spot Size (1/e2 Diameter) 360 µm
- Circularity vs. Fundamental Mode Field Diameter (MFD)
- Minimum Recommended Pulse Duration (FWHM) 15 fs
- Minimum Fundamental Pulse Duration vs. Fundamental Wavelength
- Phase Matching Bandwidth (FWHM) 97 nm
- Phase Matching Bandwidth vs. Fundamental Wavelength
- Aperture Ø5.0 mm
- Clear Aperture >80% of Diameter
- Mount Diameter 1" (25.4 mm)
- AR Coating Range 650 - 850 nm and 1300 - 1700 nm
- Reflectance Over Coating Range (Avg.) <4% at 0° AOI, Single-Layer AR Coating on Both Faces
- AR Coating Curve
- Substrate N/A
- Laser Induced Damage Threshold 0.6 J/cm2 (1550 nm, 52 fs FWHM,
S-Pol, 104 Pulses) - Surface Quality 20-10 Scratch-Dig
- Transmitted Wavefront Error λ/3 @ 632.8 nm Over Clear Aperture
| Key Specifications for SHG Applications | ||
|---|---|---|
| Item # | NLC07 | |
| Crystal Thickness | 3.00 mm | |
| Angle of Optic Axis (θ) | 19.8° | |
| AR Coating Range | 650 - 850 nm and 1300 - 1700 nm, Single-Layer Coating, Both Faces |
|
| Reflectance Over Coating Range (Avg.) | <4% at 0° AOI | |
| Fundamental Wavelength (1ω) |
AOI = 0° | 1550 nm |
| AOI Tuned | 1300 - 1700 nm | |
|
SHG Wavelength (2ω) |
AOI = 0° | 775 nm |
| AOI Tuned | 650 - 850 nm | |
| Minimum Recommended Focal Spot Size (1/e2 Diameter) |
360 µm | |
| Minimum Recommended Pulse Duration (FWHM) | 15 fs | |
| Phase Matching Bandwidth (FWHM) | 97 nm | |